Mapendekezo
NOELSON™ SFPP-600M/SFPP-800M, Rangi ya Kiwanja ya Ferro-titanium (Ace Shield Pigment LB/LC)
Anza uundaji
Mipako tajiri ya zinki ya epoxy:
| Sehemu A | ||
| Resin ya epoxy | 23 | 60% katika zilini |
| Bentone | 1 | CLAYTONE HY/HT Na Noelson Chem |
| Vumbi la zinki | 54 | 325 Mesh |
| Poda ya Ferro-fosforasi | 10 | NOELSON™ SFPP-800M, pia inaweza kubadilishwa kamili au kwa sehemu na Unga wa Compound Ferro-titanium (Ace Shield Pigment LB/LC) |
| TiO2 | ||
| Sericite mica | 2 | |
| Wollastonite | 3 | |
| Mchanganyiko wa kutengenezea | 9 | |
| Sehemu ya B | ||
| Kigumu cha resin epoxy | 100 | |
| A/B=10/1 (kwa uzani) | ||
Msingi wa zinki tajiri wa maji:
| Sehemu A | ||
| Moduli ya juu ya silicate ya lithiamu | 20-30 | |
| Standard moduli lithiamu silicate | 50-70 | |
| Sehemu ya B | ||
| Bentone | 5-10 | CLAYTONE HY/HT Na NoelsonChem |
| Plastiki | 30-40 | |
| Vumbi la zinki | 100-150 | 325 Mesh |
| Poda ya Ferro-fosforasi | 40-50 | NOELSON™ SFPP-800M, pia inaweza kubadilishwa kamili au kwa sehemu na Unga wa Compound Ferro-titanium (Ace Shield Pigment LB/LC) |
| A/B= 2.5/ 1 (kwa uzani) | ||
Notisi: Kubadilisha kipimo cha Zinki na SFPP ni kikwazo cha gharama.
Kitangulizi chenye utajiri wa zinki epoxy-polyamide:
| Sehemu A | ||
| Resin ya epoxy | 3.66 | |
| Vimumunyisho vilivyochanganywa | 10.92 | |
| Wakala wa kupambana na kutulia | 0.78 | |
| Wakala wa kukojoa | 0.32 | |
| Wakala wa kukausha | 0.66 | |
| Zinki phosphate | 3.5 | NOELSON™ ZP 409-1 |
| Poda ya Ferro-fosforasi | 19 | NOELSON™ SFPP-800M |
| Vumbi la zinki | 57.2 | |
| Sehemu ya B | ||
| Resin ya polyamide | 1.96 | |
| Vimumunyisho vilivyochanganywa | 2 | |
| A/B = 96.04:3.96 (kwa uzani) | ||